RP 600mm 24inch grafyt elektrodes foar EAF LF Smelting Steel
Technyske parameter
| Parameter | Diel | Ienheid | RP 600mm(24”) Data |
| Nominale Diameter | Elektrode | mm (inch) | 600 |
| Max Diameter | mm | 613 | |
| Min Diameter | mm | 607 | |
| Nominale lingte | mm | 2200/2700 | |
| Max Length | mm | 2300/2800 | |
| Min Length | mm | 2100/2600 | |
| Max Stromdichtheid | KA/cm2 | 11-13 | |
| Aktuele draachkapasiteit | A | 30000-36000 | |
| Spesifike ferset | Elektrode | μΩm | 7,5-8,5 |
| Nippel | 5,8-6,5 | ||
| Flexural sterkte | Elektrode | Mpa | ≥8,5 |
| Nippel | ≥16,0 | ||
| Young's Modulus | Elektrode | Gpa | ≤9,3 |
| Nippel | ≤13,0 | ||
| Soartlik gewicht | Elektrode | g/cm3 | 1,55-1,64 |
| Nippel | ≥1,74 | ||
| CTE | Elektrode | ×10-6/℃ | ≤2.4 |
| Nippel | ≤2.0 | ||
| Ash ynhâld | Elektrode | % | ≤0.3 |
| Nippel | ≤0.3 |
OPMERKING: Elke spesifike eask foar diminsje kin wurde oanbean.
Hoe Underhâld Foar Graphite Electrode
Neist it selektearjen fan de juste RP-grafytelektrode, is ûnderhâld essensjeel om de langstme en effisjinsje fan 'e elektrode te garandearjen.Goede ôfhanneling en opslach fan 'e elektrodes binne krúsjaal om it risiko fan elektrode-oksidaasje, sublimaasje, ûntbining, spalting en brekken te minimalisearjen.As de elektrode wurdt brûkt, moat de ovenoperator omtinken jaan oan de slijtage fan 'e elektrode en de posysje fan' e elektrode en de ynput fan 'e elektrodes oanpasse.Goede ynspeksje nei ûnderhâld, ynklusyf fisuele ynspeksje en testen fan elektryske konduktiviteit, kin ek helpe by it identifisearjen fan potinsjele skea of fersmoarging fan 'e elektrode.
Ynstruksje oerleverje en gebrûk foar grafytelektroden
- Brûk de spesjale lifting ark om it libben fan 'e grafytelektrode te foarkommen dat se skea tidens ferfier wurde.(sjoch pic1)
- Graphite elektrode moat wurde hâlden fuort fan fochtige of wiet troch rein, snie, wurde hâlden droech. (sjoch pic2)
- Kontrolearje foarsichtich foar gebrûk, soargje derfoar dat de socket en nipple thread geskikt binne foar gebrûk, ynklusyf ynspeksje foar pitch, plug. (sjoch pic3)
- Reinigje de tepel en sockets triedden mei komprimearre loft. (sjoch pic4)
- Foar gebrûk moat de grafytelektrode yn 'e oven droege wurde, de droegetemperatuer moat minder dan 150 ℃ wêze, de droege tiid moat mear dan 30 oeren wêze. (sjoch pic5)
- Grafytelektrode moat strak en rjocht wurde ferbûn mei passende draaimoment.(sjoch pic6)
- Om it brekken fan 'e grafytelektrode te foarkommen, set it grutte diel yn legere posysje en lyts diel yn' e boppeste posysje.
RP Graphite Electrode Aktuele draachkapasiteit Chart
| Nominale Diameter | Regular Power (RP) Grade Graphite Elektrode | ||
| mm | Inch | Aktuele draachkapasiteit (A) | Aktuele tichtens (A/cm2) |
| 300 | 12 | 10000-13000 | 14-18 |
| 350 | 14 | 13500-18000 | 14-18 |
| 400 | 16 | 18000-23500 | 14-18 |
| 450 | 18 | 22000-27000 | 13-17 |
| 500 | 20 | 25000-32000 | 13-16 |
| 550 | 22 | 28000-36000 | 12-15 |
| 600 | 24 | 30000-36000 | 11-13 |
Relatearre produkten
-
UHP 450mm Oven grafyt elektrodes mei Nipp ...
Technyske parameter Parameter Part Unit UHP 450mm(18”) Gegevens Nominale Diameter Elektrode mm(inch) 450(18) Maks Diameter mm 460 Min Diameter mm 454 Nominale lingte mm 1800/2400 Max Length mm 1900/25100 Min Max Length/mm 3 Stromdichtheid KA/cm2 19-27 Stromdrachkapasiteit A 32000-45000 Spesifike wjerstânselektrode μΩm 4.8-5.8 Nippel 3.4-3.8 F...
-
Lytse Diameter 225mm Furnace Graphite Elektrode ...
Technyske Parameter Chart 1: Technyske parameter Foar Lytse Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g / cm3 × 10-6 / ℃ % 3 75 Elektrode 7,5-8,5 ≥9,5 ≥9. -1.64 ≤2.4 ≤0.3 Nippel 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Elektrode 7.5-8.5 ≥9.0 ≤ 5.0 ≤1. .3 Nip...
-
Lytse diameter oven grafyt elektrodes foar e ...
Technyske Parameter Chart 1: Technyske parameter Foar Lytse Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g / cm3 × 10-6 / ℃ % 3 75 Elektrode 7,5-8,5 ≥9,5 ≥9. -1.64 ≤2.4 ≤0.3 Nippel 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Elektrode 7.5-8.5 ≥9.0 ≤ 5.0 ≤1. .3 Nip...
-
Grafytelektroden brûkt stielmakkerij mei nippel ...
Technical Parameter Parameter Part Unit RP 500mm(20”) Data Nominale Diameter Elektrode mm(inch) 500 Max Diameter mm 511 Min Diameter mm 505 Nominale Lengte mm 1800/2400 Max Length mm 1900/2500 Min Length mm Dens 1000 KA / Strom /cm2 13-16 Aktuele draachkapasiteit A 25000-32000 Spesifike wjerstânselektrode μΩm 7.5-8.5 Nippel 5.8-6.5 Flexur...
-
Grafytelektroden in elektrolyse HP 450mm 18...
Technyske parameter Parameter Part Unit HP 450mm(18”) Gegevens Nominale Diameter Elektrode mm(inch) 450 Max Diameter mm 460 Min Diameter mm 454 Nominale Lengte mm 1800/2400 Max Length mm 1900/2500 Min Length mm 100KA Strom/2s cm2 15-24 Aktuele draachkapasiteit A 25000-40000 Spesifike wjerstânselektrode μΩm 5.2-6.5 Nippel 3.5-4.5 Flexural S...
-
High Purity Sic Silicon Carbide Crucible Graphi ...
Silicon Carbide Crucible Performance Parameter Data Parameter Data SiC ≥85% Cold Crushing Strength ≥100MPa SiO₂ ≤10% Skynbere porositeit ≤%18 Fe₂O₃ <1% Temperatuer Resistance ≥1700°C ≥1700°C Prachtige termyske konduktiviteit --- It hat poerbêste termyske ...